This product is a waterproof repair material with certain impermeability properties made by mixing a variety of functional additives modified polymer, special cementitious materials, and high-quality aggregates in proportion. The production and use process is non-toxic, pollution-free, environmentally friendly, with good adhesion to the base, good fluidity, no shrinkage, and good crack resistance. Widely used for waterproof repair and reinforcement of damp concrete structures, especially suitable for waterproof and anti-seepage construction of tunnels, subways, dams, etc.

一、Product Introduction
This product is a waterproof repair material with certain impermeability properties made by mixing a variety of functional additives modified polymer, special cementitious materials, and high-quality aggregates in proportion. The production and use process is non-toxic, pollution-free, environmentally friendly, with good adhesion to the base, good fluidity, no shrinkage, and good crack resistance. Widely used for waterproof repair and reinforcement of damp concrete structures, especially suitable for waterproof and anti-seepage construction of tunnels, subways, dams, etc.
二、Main characteristics
Good adhesion performance, compactness, and waterproof performance;
Convenient construction, can be carried out on damp substrates and under low temperature conditions;
Corrosion resistance, high temperature resistance, low temperature resistance, and aging resistance;
Non deteriorating, earthquake resistant, non-toxic and harmless, odorless, green and environmentally friendly. If there is no human or structural damage, it has the same lifespan as the building;
High adhesive strength and good affinity with various wall substrates (such as coatings, tiles, etc.);
Stable quality, easy construction, and can be applied by directly adding water and stirring on site;
A good interface layer is formed on the surface layer, which facilitates subsequent construction. Save labor and time, reduce overall costs.
三、Technical Parameter
Serial number |
entry |
Dry powder |
|
1 |
Setting time |
Initial setting /min Final coagulation /h |
≥45 ≤2 |
2 |
Impermeability pressure /MPa |
7d 28d |
≥1 ≥1.5 |
3 |
Compressive strength /MPa |
28d |
≥45 |
4 |
Flexural strength |
28d |
≥12 |
5 |
Bond strength |
7d 28d |
≥1 ≥1.2 |
6 |
Alkaline resistant saturated Ca(OH)₂ solution |
168h |
No cracking or peeling |
7 |
Heat resistance (100℃ water) |
5h |
No cracking or peeling |
8 |
Frost resistance - freeze-thaw cycle (-15℃~+20℃) |
25 times |
No cracking or peeling |
9 |
Shrinkage rate /% |
28d |
≤0.15 |
四、Application scope
Waterproof repair of tunnels, subways, and highway bridges;
Repair and leakage repair of industrial and civil building basements, repair of leakage on building roofs and interior and exterior walls, waterproofing and anti-seepage of various water pools, civil air defense projects, tunnels, grain warehouses, bathrooms, kitchens, factories, and enclosed balconies;
Surface sealing, waterproofing, and anti-seepage of aerated concrete slabs;
Application as an interface treatment agent.
五、Packaging specifications
Under normal storage conditions, the storage period is 90 days. If it exceeds 90 days, it must be verified through testing before use;
25kg/pack or according to user requirements.
六、Precautions
During construction, the base layer should be cleaned to keep it flat, clean, and free of dirt;
Moisturizing and maintenance are necessary during final setting.
七、Usage
Add 15-25kg of clean water to 100kg of repair mortar and stir to form a uniform paste like material;
Reference dosage: 3mm thick 5kg/m2.
八、Typical applications